Influence of oxygen on the growth of cubic boron nitride thin films by plasma-enhanced chemical vapour deposition

Cubic boron nitride thin films were deposited on silicon substrates by low-pressure inductively coupled plasma-enhanced chemical vapour deposition. It was found that the introduction of O2 into the deposition system suppresses both nucleation and growth of cubic boron nitride. At a B2H6 concentration of 2.5% during film deposition, the critical O2 concentration allowed for the nucleation of cubic boron nitride was found to be less than 1.4%, while that for the growth of cubic boron nitride was higher than 2.1%. Moreover, the infrared absorption peak observed at around 1230–1280 cm−1, frequently detected for cubic boron nitride films prepared using non-ultrahigh vacuum systems, appears to be due to the absorption of boron oxide, a contaminant formed as a result of the oxygen impurity. Therefore, the existence of trace oxygen contamination in boron nitride films can be evaluated qualitatively by this infrared absorption peak. (condensed matter: electronic structure, electrical, magnetic, and optical properties)