Nanoscale structural and electrical properties of graphene grown on AlGaN by catalyst-free chemical vapor deposition

The integration of graphene (Gr) with nitride semiconductors is highly interesting for applications in high-power/high-frequency electronics and optoelectronics. In this work, we demonstrated the direct growth of Gr on Al_0.5Ga_0.5N/sapphire templates by propane (C₃H₈) chemical vapor deposition at a temperature of 1350 °C. After optimization of the C₃H₈ flow rate, a uniform and conformal Gr coverage was achieved, which proved beneficial to prevent degradation of AlGaN morphology. X-ray photoemission spectroscopy revealed Ga loss and partial oxidation of Al in the near-surface AlGaN region. Such chemical modification of a ∼2 nm thick AlGaN surface region was confirmed by cross-sectional scanning transmission electron microscopy combined with electron energy loss spectroscopy, which also showed the presence of a bilayer of Gr with partial sp²/sp³ hybridization. Raman spectra indicated that the deposited Gr is nanocrystalline (with domain size ∼7 nm) and compressively strained. A Gr sheet resistance of ∼15.8 kΩ sq⁻¹ was evaluated by four-point-probe measurements, consistently with the nanocrystalline nature of these films. Furthermore, nanoscale resolution current mapping by conductive atomic force microscopy indicated local variations of the Gr carrier density at a mesoscopic scale, which can be ascribed to changes in the charge transfer from the substrate due to local oxidation of AlGaN or to the presence of Gr wrinkles. (paper)