Express evaluation of high-temperature strength of casting TiAl-base alloys

Creators

  • 1. RAN, Inst. Metallurgii i Materialovadeniya im. A.A. Bajkova, Moscow (Russian Federation)

Description

The hot strength of the casting TiAl alloys by the temperature up to 1000 Deg C is determined. The effect of alloying on the TiAl strength is carried out through the hot strength method. The comparison of the obtained data with the data of the effect of alloying on their strength characteristics is carried out. It is shown that both the yield limits and their hot hardness values at the temperatures below 900 Dec C are closely related and the areas of their values are partially overlapped. It is shown, that the TiAl alloys at the temperatures above 900 Deg C are weakening faster with the temperature growth that the Ni3Al alloys within the same temperature range

Abstract (Russian)

Определена горячая твердость при температурах до 1000 град С литейных сплавов TiAl. Проведено изучение методом горячей твердости влияния легирования на твердость сплавов TiAl. Выполнено сравнение полученных данных с данными о влиянии легирования на характеристики их прочности. Показано, что как пределы текучести, так и значения их горячей твердости при температурах менее 900 град С близки, и области их значений частично перекрываются. Показано, что сплавы TiAl при температурах выше 900 град С разупрочняются быстрее с повышением температуры, чем сплавы Ni3Al в том же температурном интервале

Additional details

Additional titles

Original title (Russian)
Экспрессная оценка жаропрочности литейных сплавов на основе TiAl

Publishing Information

Journal Title
Metally (Moscow)
Journal Issue
no.1
Journal Page Range
p. 91-98
ISSN
0869-5733
CODEN
MEALET

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
35046159
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
ALUMINIUM ALLOYS; CASTING; HAFNIUM ALLOYS; HARDNESS; HEAT RESISTING ALLOYS; NICKEL ALLOYS; ORDER-DISORDER TRANSFORMATIONS; TITANIUM ALLOYS; YIELD STRENGTH; ZIRCONIUM ALLOYS
Descriptors DEC
ALLOYS; FABRICATION; HEAT RESISTANT MATERIALS; MATERIALS; MECHANICAL PROPERTIES; PHASE TRANSFORMATIONS; TRANSITION ELEMENT ALLOYS

Optional Information

Notes
24 refs.; 5 figs.; 1 tab.