Study of the pore-opening process of latent tracks of light low-energetic ions in CR-39 by means of electrolytic etching
Description
In this thesis the irradiation of 10-μm thick CR-39 foils with 5.5-7 MeV protons and of 22-400 μm thick CR-39 foils with 4.85-28 MeV α-particles with subsequent determination of the etching velocities is described. By means of scanning electron microscopy (SEM) the pore shape after irradiation was determined. From the analysis of the track profiles by means of SEM the track-nucleus diameter for 28 MeV α particles was determined to 1.4 nm. (HSI)
Additional details
Additional titles
- Original title (German)
- Untersuchung des Porenoeffnungsprozesses latenter Spuren leichter niederenergetischer Ionen in CR-39 mittels elektrolytischer Aetzung
Identifiers
Publishing Information
- Imprint Pagination
- 107 p.
- University
- TU Dresden
- Degree
- PhD
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 37022321
- Subject category
- S36: MATERIALS SCIENCE;
- Resource subtype / Literary indicator
- Thesis, Non-conventional Literature
- Descriptors DEI
- ALPHA PARTICLES; CHEMICAL REACTION KINETICS; ELECTROLYSIS; ETCHING; FOILS; ION COLLISIONS; MEV RANGE 01-10; MEV RANGE 10-100; PARTICLE TRACKS; PHYSICAL RADIATION EFFECTS; POLYCARBONATES; PORE STRUCTURE; PROTONS; SCANNING ELECTRON MICROSCOPY; THIN FILMS
- Descriptors DEC
- BARYONS; CARBON COMPOUNDS; CARBONATES; CHARGED PARTICLES; COLLISIONS; ELECTRON MICROSCOPY; ELEMENTARY PARTICLES; ENERGY RANGE; FERMIONS; FILMS; HADRONS; IONIZING RADIATIONS; KINETICS; LYSIS; MEV RANGE; MICROSCOPY; MICROSTRUCTURE; NUCLEONS; ORGANIC COMPOUNDS; ORGANIC POLYMERS; OXYGEN COMPOUNDS; POLYMERS; RADIATION EFFECTS; RADIATIONS; REACTION KINETICS; SURFACE FINISHING