Strength behaviour of 10CrMo9.10 steel in nonsteady-state applications

2 testing runs with cyclic temperature increase were conducted on steel 10CrMo9.10 samples, i.e., at 500 degC and cyclic increase by 10, 25 and 50 degC, and at 550 degC and cyclic increase by 50 degC. Long-term strength was studied under a strain of 6.1 to 25.6 kp/mm2 for 22,000 hours and the effect of periodical unloading was investigated on long-term strength at 550 degC. Sample loading and unloading proceeded within the range of 8.8 to 24.7 kp/mm2 at an unloading rate of 8 to 100 %/min. Steel lifetime was not affected by the number of cycles. The effect of the changing load and of constant temperature without load on the long-term strength of the steel at 550 degC is shown graphically. The results showed a clear dependence of steel life on dwell time at the given temperature without load. (J.P.)