Evaluation of the release behavior of the dexamethasone embedded in polycarbonate polyurethane membranes: an in vitro study

To evaluate the release behavior of dexamethasone embedded in a polycarbonate polyurethane membrane. Both water-soluble and water-insoluble dexamethasone were tested, and the release behavior of five water-insoluble dexamethasone films of different thickness (78 to 211 μm) was also evaluated. The amount of dexamethasone used was 10% of the total weight of the polyurethan film mass. Each film was placed in a centrifuge tube containing 25 ml of 0.1-M neutral phosphate buffer, and the tubes were placed in a shaking incubator to quantify the amount of drug released into the buffer, absorption spectroscopy (λ max=242 nm) was employed. In the test involving water-soluble dexamethasone, 60%, of the drug was released during the first two hours of the study. Films containing water-insoluble dexamethasone, on the other hand, released 40%, 60% and 75% of the dexamethasone in one, three and seven days, respectively. Both types of film maintained low-dose drug release for 28 days. When release behavior was compared between water-insoluble films of different thickness, thicker film showed less initial burst and more sustained release. Dexamethasone release behavior varies according to drug solubility and membrane thickness, and may thus be conrolled