Insights into the microstructural and physical properties of colloidal Fe:ZnSe nanocrystals

Highlights: • We present a facile and environmentally friendly protocol to fabricate Fe:ZnSe nanocrystals. • The microstructural and physical properties of Fe:ZnSe nanocrystals were systematically investigated. • The current synthesis is dramatically simple and highly reproducible, it will facilitate the commercial scale synthesis of highly luminescent water-soluble nanocrystals with surface functionality in the near future. - Abstract: Here, we present a facile and environmentally friendly synthetic protocol to fabricate highly luminescent and water-soluble Fe:ZnSe nanocrystals in aqueous solution at low temperature. The microstructure and various physical properties (e.g., crystal structure, interplanar spacing, lattice parameter, crystalline size, lattice microstrain, intrinsic stress, X-ray density, specific surface area, dislocation density, porosity, agglomeration number) of the Fe:ZnSe nanocrystals were systematically investigated using X-ray diffraction. The particle size and morphology of the Fe:ZnSe nanocrystals were determined by transmission electron microscopy. The optical properties (e.g., absorption and photoluminescence) of the fabricated nanocrystals were explored using ultraviolet–visible absorption and photoluminescence spectroscopies, respectively. The surface functionalization of the Fe:ZnSe nanocrystals by mercaptoacetic acid ligand was evidenced by Fourier transform infrared spectroscopy. To confirm the elementary composition of the obtained nanocrystals, Energy dispersive X-ray spectroscopy was performed. To further shed light upon elemental distribution of the resulting nanocrystals, elemental mapping measurements were conducted. Moreover, the underlying mechanisms were also elucidated. As a consequence, the current investigation not only provides a deep insight into exploring the physical properties of doped nanocrystals, but also demonstrates a useful synthetic strategy for producing water-soluble and highly fluorescent doped nanocrystals