Color centers in neutron-irradiated Y3Al5O12, CAF2 and LiF single crystals

The thermal annealing behavior of the Y3Al5O12, CaF2 and LiF single crystals bombarded at Algiers with reactor neutrons has been monitored by optical absorption spectroscopy. The irradiation was performed at about 315 K. On heating samples after irradiation, the optical absorption bands decrease and disappear completely at 873 and 523 K in the case of Y3Al5O12 and CaF2, respectively. Activation energies of 1.2±0.02 and 0.9±0.2 eV are estimated for Y3Al5O12 and CaF2, respectively. On the other hand, the LiF crystal shows a complex annealing behavior. Here, the optical absorption spectrum presents different shapes after each annealing temperature. Four steps are distinguished and discussed on heating samples from 300 to 673 K. Above 673 K, the absorption drops by about 50%; it completely disappears at 773 K