Study of the optical properties and the carbonaceous clusters in thermally-annealed CR-39 and Makrofol-E polymer-based solid-state nuclear track detectors

The induced modifications in the optical properties of CR-39 and Makrofol-E polymer-based solid state nuclear track detectors were investigated after thermal annealing at a temperature of 200 .deg. C for different durations. The optical properties were studied using an UV-visible spectrophotometer. From the UV-visible spectra, the direct and the indirect optical band gaps, Urbach's energies, and the number of carbon atoms in a cluster were determined. The absorbance of CR-39 plastic detector was found to decrease with increasing annealing time while the absorbance of Makrofol-E decreased with increasing annealing time. The width of the tail of localized states in the band gap ΔE was evaluated with the Urbach method. The optical energy band gaps were obtained from the direct and the indirect allowed transitions in K-space. Both of the direct and the indirect band gaps of the annealed CR-39 detector decrease with increasing annealing time while in Makrofol-E, they decreased after an annealing time of 15 minute and then showed no remarkable changes for a prolonged annealing times. Urbach's energy decreased significantly for both CR-39 and Makrofol-E with increasing annealing time. The number of carbon atoms in a cluster increased in the CR-39 detector with increasing annealing time while it decreased with increasing annealing time for Makrofol-E. We may conclude that the CR-39 detector undergoes greater modifications than the Makrofol-E detector upon thermal annealing at 200 .deg. C. In conclusion, the induced modifications in the optical properties of CR-39 and Makrofol-E are correlated with the temperature and the duration of annealing.