Operational damage of steel 12Kh1MF steam superheater tubes

Creators

Description

The structure and mechanical properties of steel 12Kh1MF specimens are investigated after cyclic tests under conditions simulating operational regime of steam superheater tubes. It is revealed that in thermal barocycling a decrease of steel strength and a transition from trans crystalline to intercrystalline feature take place due to precipitation of complex carbides along grain boundaries. Complex carbide formation is resulted from the appearance of free carbon of decomposed carbon-containing organic impurities in a water coolant

Abstract (Russian)

Проведены исследования структуры и механических свойств образцов стали 12Х1МФ после циклических испытаний в условиях, моделирующих эксплуатацилнный режим труб пароперегревателей. Устанволено, что в процессе термобароциклирования происходит разупрочнение стали и переход от транскристаллитного к интеркристаллитному разрушению в результате выделения сложных карбидов по границам зерен. Образование сложных карбидов является следствием поступления свободного углерода при разложении углеродсодержащих органических примесей в воде

Additional details

Additional titles

Original title (Russian)
Эксплуатационные повреждения труб пароперегревателей из стали 12Kh1MF

Publishing Information

Journal Title
Izvestiya Vysshikh Uchebnykh Zavedenij. Chernaya Metallurgiya
Journal Issue
no.6
Journal Page Range
p. 38-41
CODEN
IVUMAX

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
31020500
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
DUCTILE-BRITTLE TRANSITIONS; FEEDWATER; FRACTURES; IMPURITIES; STEEL-CR12MOV; SUPERHEATERS; SURFACTANTS; TEMPERATURE RANGE 0400-1000 K; TENSILE PROPERTIES; THERMAL CYCLING; VERY HIGH PRESSURE; WATER CHEMISTRY
Descriptors DEC
ALLOYS; CARBON ADDITIONS; CHEMISTRY; CHROMIUM ALLOYS; CHROMIUM STEELS; CORROSION RESISTANT ALLOYS; FAILURES; HEAT RESISTANT MATERIALS; HEAT RESISTING ALLOYS; HIGH ALLOY STEELS; HYDROGEN COMPOUNDS; IRON ALLOYS; IRON BASE ALLOYS; MARTENSITIC STEELS; MATERIALS; MECHANICAL PROPERTIES; MOLYBDENUM ADDITIONS; OXYGEN COMPOUNDS; STAINLESS STEELS; STEELS; TEMPERATURE RANGE; TRANSITION ELEMENT ALLOYS; VANADIUM ADDITIONS; WATER

Optional Information

Notes
7 refs., 2 figs.