Erosion corrosion in a wet steam loop
Creators
- 1. Technischer Ueberwachungs-Verein Rheinland e.V., Koeln (Germany, F.R.). Inst. fuer Materialpruefung und Chemie
Description
In a technical loop of a power plant erosion corrosion behaviour of the steels C 22.8, 15 Mo 3 and 10 Cr Mo 9 10 was investigated in test periods up to 78 days under definite conditions in wet steam of a relative steam content of about 75% at a temperature of 185 to 2000C and flow velocities up to 180 m/s. For comparison one test was carried out also in hot steam. By gravimetric, metallographic, SEM- and X-ray-diffraction analysis essential information was obtained on the kinetics of erosion corrosion and the structure of oxide coatings. The rate of erosion corrosion shows a high dependence on time and steel composition and decrease in the above mentioned order. Structure and quality of the oxide layer also show a remarkable dependence on steel composition. (orig.)
Abstract (German)
In einer grosstechnischen Versuchsstrecke eines Kraftwerkes wurde das Erosionskorrosions-Verhalten der Werkstoffe C 22.8, 15 Mo 3 und 10 Cr Mo 9 10 in Nassdampf mit einem relativen Dampfgehalt von etwa 75% bei 185-2000C bei Stroemungsgeschwindigkeiten bis zu 180 m/s in Langzeitversuchen (bis zu 78 Tagen) untersucht. Vergleichsweise wurde auch die Beanspruchung durch Heissdampf mit in die Untersuchungen einbezogen. Durch gravimetrische, metallografische, REM- und Roentgenfeinstruktur-Untersuchungen wurden wesentliche Erkenntnisse zum zeitlichen Verlauf der Erosionskorrosion sowie ueber den Aufbau der Oxidschichten erhalten. Der Abtrag durch Erosionskorrosion zeigt eine starke Zeitabhaengigkeit und nimmt in der o.a. Reihenfolqe der Werkstoffe deutlich ab. Struktur und Eigenschaften der Oxidschichten lassen ebenfalls eine deutliche Abhaengigkeit von der Strahlzusammensetzung erkennen. (orig.)Additional details
Additional titles
- Original title (German)
- Erosionskorrosions-Untersuchungen in einer Nassdampfversuchsstrecke
Publishing Information
- Journal Title
- Werkst. Korros.
- Journal Volume
- 33
- Journal Issue
- 1
- Series
- Werkst. Korros.
- Journal Page Range
- 14-24
- ISSN
- 0043-2822
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 13683306
- Subject category
- S37: INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; S42: ENGINEERING;
- Descriptors DEI
- CARBON STEELS; CHEMICAL COMPOSITION; COATINGS; CORROSION; ELECTRON MICROSCOPY; ELECTRON SCANNING; EROSION; FLOW RATE; HIGH TEMPERATURE; LOSSES; MASS; MATERIALS TESTING; METALLOGRAPHY; MICROSTRUCTURE; OXIDES; PILOT PLANTS; REACTION KINETICS; STEAM; TIME DEPENDENCE; X-RAY DIFFRACTION
- Descriptors DEC
- ALLOYS; CARBON ADDITIONS; CHALCOGENIDES; CHEMICAL REACTIONS; COHERENT SCATTERING; CRYSTAL STRUCTURE; DIFFRACTION; FUNCTIONAL MODELS; IRON ALLOYS; IRON BASE ALLOYS; KINETICS; MICROSCOPY; OXYGEN COMPOUNDS; SCATTERING; STEELS; TESTING; TRANSITION ELEMENT ALLOYS