Magnetic properties and microstructure of nanocrystalline soft magnetic Fe73.5-xCoxCu1Nb3Si13.5B9 alloys

Creators

  • 1. UrO RAN, Inst. Fiziki Metallov, Ekaterinburg (Russian Federation)

Description

Magnetic parameters of nanocrystalline alloys of Fe73.5-xCoxCu1Nb3Si13.5B9 (x=0, 10, 20, 30) are studied depending on annealing temperature, cooling rate, magnetic field frequency on thermomagnetic treatment. It is revealed that thermomagnetic treatment of Co bearing nanocrystalline alloys in a constant magnetic field gives rise to the displacement of a hysteresis loop. The hysteresis loop displacement field increases with a Co content in the alloy which is supposedly associated with precipitation of α-Co, β-Co clusters and (Fe,Co)3Si, (Fe,Co)3B nanophases, the direction of magnetization in these phases is determined by the orientation of magnetic field on thermomagnetic treatment

Abstract (Russian)

Исследовано влияние температуры отжига, скорости охлаждения, частоты магнитного поля при термомагнитной обработке на магнитные параметры нанокристаллических сплавов Fe73.5-xCoxCu1Nb3Si13.5B9 (x=0, 10, 20, 30). Обнаружено, что термомагнитная обработка в постоянном магнитном поле в нанокристаллических сплавах, содержащих Co, приводит к смещению петли гистерезиса. С повышением содержания Co в сплаве поле смещения петли гистерезиса увеличивается, что, по-видимому, связано с выделением кластеров α-Co, β-Co и нанофаз (Fe,Co)3Si, (Fe,Co)2B, направление намагниченности в которых определяется направлением магнитного поля при термомагнитной обработке

Additional details

Additional titles

Original title (Russian)
Магнитные свойства и микроструктура нанокристаллических магнитомягких сплавов Фе

Publishing Information

Journal Title
Fizika Metallov i Metallovedenie
Journal Volume
102
Journal Issue
5
Journal Page Range
p. 539-544
ISSN
0015-3230
CODEN
FMMEA9

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
38056008
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
ANNEALING; BORON ALLOYS; CHEMICAL COMPOSITION; COBALT ALLOYS; COERCIVE FORCE; COPPER ALLOYS; DOMAIN STRUCTURE; GRAIN SIZE; HYSTERESIS; IRON BASE ALLOYS; MAGNETIC FIELDS; MAGNETIC PROPERTIES; METALLIC GLASSES; NIOBIUM ALLOYS; SILICON ALLOYS; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 0400-1000 K
Descriptors DEC
ALLOYS; HEAT TREATMENTS; IRON ALLOYS; MICROSTRUCTURE; PHYSICAL PROPERTIES; SIZE; TEMPERATURE RANGE; TRANSITION ELEMENT ALLOYS

Optional Information

Notes
8 refs., 6 figs., 2 tabs.