Study of clean and ion bombardment damaged silver single crystal surfaces by work function measurements

Work function values of the (110), (100) and (111) faces of silver single crystal were measured by the photoelectric emission method and found to be 4.14 +- 0.04 eV, 4.22 +-0.04 eV and 4.46 +- 0.02 eV respectively. Oxygen adsorption on the faces were studied by surface potential measurement. Strong oxygen adsorption was observed on (110) and (100) faces, whereas the (111) face was found to be inert for oxygen adsorption. Oxygen adsorption on the (111) face damaged by argon ion bombardment was also investigated. The above results were compared with those of early reported work function and oxygen adsorption values. (U.K.)