The effect of thermal history on crystalline structure and mechanical properties of β-nucleated isotactic polypropylene

The effect of thermal history on β-nucleated iPP was systematically investigated by comparing the variance of crystalline microstructures and mechanical property of stepwise crystallized sample and annealed sample, which experienced different thermal history. The mechanical property tests exhibit that that the toughness of stepwise crystallized sample and annealed sample were both decreased compared to control sample, while the tensile strength of the stepwise crystallized sample increased slightly. Structure investigation showed that the α-relaxation peak, which is related to the assignment of chains in rigid amorphous phase, moved to the high temperature region for stepwise crystallized sample, while it moved to the low temperature region for annealed sample. The results indicated the weakening in rigid amorphous fraction (RAF) and the increase in lamellar thickness of β-iPP after stepwise crystallization treatment. For annealed sample, the RAF strengthened and lamellar thickness decreased slightly after thermal treatment. A mechanism of crystalline microstructures evolution of restricted area between the main lamellar under different treatments was proposed. (paper)