Microstructures and mechanical properties evolution of an Al–Fe–Cu alloy processed by repetitive continuous extrusion forming

Repetitive continuous extrusion forming process (R-Conform process), as a continuous severe plastic deformation method, was performed on a horizontal continuous casting Al–0.74Fe–0.23Cu alloy. The microstructural evolution and mechanical properties were studied by optical microscope, X-ray diffraction, scanning electron microscope, transmission electron microscope, and tensile testing. The results show that tensile ductility of the Al–0.74Fe–0.23Cu alloy is greatly improved but tensile strength is gradually decreased after repetitive Conform processing. The necking is more intense and the size of dimples becomes bigger with increasing Conform passes. The first pass Conform process induces obviously grains refining, dissolution of AlFe, AlFeSi and AlSi primary phases, strain-induced precipitation and transformation of crystal orientation distributions, but further Conform deformation only changes the redistribution of precipitates. The changes of mechanical properties may be attributed to a complex progress of recovery, recrystallization and redistribution of precipitates during repetitive Conform process