Anisotropic changes induced by ion irradiation on Bi-based high Tc superconductors
- 1. Middle East Technical Univ., Ankara (Turkey)
- 2. King Fahd Univ. of Petroleum and Minerals, Dhahran (Saudi Arabia)
Description
(Bi,Pb)2Sr2Ca2Cu3O10 high Tc superconducting samples were subject to irradiation by 7 MeV Si ions. X-ray diffraction analysis showed that the intensity of the (00l) peaks decrease rapidly with ion irradiation, while that of the mixed index peaks (hkl) changes very little. The a-parameter decreases first then increases with ion fluence while the c-parameter increase continuously with ion irradiation. (Author)
Additional details
Publishing Information
- Journal Title
- Solid State Communications
- Journal Volume
- 87
- Journal Issue
- 12
- Journal Page Range
- p. 1129-1131.
- ISSN
- 0038-1098
- CODEN
- SSCOA4
INIS
- Country of Publication
- United Kingdom
- Country of Input or Organization
- United Kingdom
- INIS RN
- 25005614
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- ANISOTROPY; ATOMIC DISPLACEMENTS; BISMUTH ADDITIONS; BISMUTH OXIDES; CALCIUM OXIDES; COPPER OXIDES; CRYSTAL-PHASE TRANSFORMATIONS; HIGH-TC SUPERCONDUCTORS; ION BEAMS; LATTICE PARAMETERS; LEAD OXIDES; MEV RANGE 01-10; MICROSTRUCTURE; SILICON IONS; STRONTIUM OXIDES; X-RAY DIFFRACTION
- Descriptors DEC
- ALKALINE EARTH METAL COMPOUNDS; BEAMS; BISMUTH COMPOUNDS; CALCIUM COMPOUNDS; CHALCOGENIDES; CHARGED PARTICLES; COHERENT SCATTERING; COPPER COMPOUNDS; CRYSTAL STRUCTURE; DIFFRACTION; ENERGY RANGE; IONS; LEAD COMPOUNDS; MEV RANGE; OXIDES; OXYGEN COMPOUNDS; PHASE TRANSFORMATIONS; PHYSICAL RADIATION EFFECTS; RADIATION EFFECTS; SCATTERING; STRONTIUM COMPOUNDS; SUPERCONDUCTORS; TRANSITION ELEMENT COMPOUNDS