Influence of nitrogen on the corrosion behaviour of solution treated and annealed austenitic 18/10 chromium-nickel and 18/12 chromium-nickel-molybdenum steels. Pt. 1
Creators
- 1. Mannesmann-Forschungsinstitut G.m.b.H., Duisburg (F.R. Germany)
Description
Investigations into the corrosion behaviour of CrNi steels with (weight-%) 0.019-0.029 C, 18.5 Cr, 11 Ni, 0.022-0.138 N and 0.020 to 0.031 C, 17.2 Cr, 13 Ni, 2.6 Mo, 0.028 to 0.130 N by the Strauss-Test, the Strauss-Test under rigid condition and the Huey-Test. The first part of this paper is devoted in particular to the analysis of structural constituents and in particular to precipitations. In the molybdenum-free steel heat treatment results in precipitation of M23C6 and Cr2N, the precipitation of the first being independent from nitrogen content. In the case of the molybdenum-bearing steels the precipitation of M23C6 is independent from nitrogen content too but is shifted toward higher temperatures. The precipitation of Cr2N is slowed down by Mo. The precipitation of other phases (chi-, sigma- and Z-phases) is affected differently by nitrogen. (orig.)
Abstract (German)
Untersuchungen über das Korrosionsverhalten von CrNi‐Stählen mit (Gew. ‐%) 0,019–0,029 C, 18,5 Cr, 11 Ni, 0,022–0,138 N sowie 0,020–0,031 C, 17,2 Cr, 13 Ni, 2,6 Mo, 0,028–0,130 N nach dem Strauß‐Test, dem verschärften Strauß‐Test und dem Huey‐Test. Der erste Teil der Arbeit ist vor allem der Untersuchung der Gefügebestandteile und vor allem der Ausscheidungen gewidmet. Im molybdänfreien Stahl wird nach Wärmebehandlung neben M 23 C 6 auch Cr 2 N gefunden; die Ausscheidung des ersten Carbids wird vom Stickstoff nicht beeinflußt. Im Falle der Mo‐haltigen Stähle ist die Ausscheidung von M 23 C 6 ebenfalls unabhängig vom Stickstoffgehalt, jedoch nach höheren Temperaturen verschoben; die Ausscheidung von Cr 2 N wird durch Mo verlangsamt. Auch die Ausscheidung anderer Phasen (Chi‐, Sigma‐ und Z‐Phase) wird durch den Stickstoff unterschiedlich beeinflußt.Additional details
Additional titles
- Subtitle (English)
- Precipitation behaviour of the steels
- Original title (German)
- Der Einfluss von Stickstoff auf die korrosionschemischen Eigenschaften loesungsgegluehter und angelassener austenitischer 18/10 Chrom-Nickel- und 18/12 Chrom-Nickel- und 18/12 Chrom-Nickel-Molybdaen-Staehle. T. 1
- Original subtitle (German)
- Ausscheidungsverhalten der Staehle.
Identifiers
Publishing Information
- Journal Title
- Materials and Corrosion
- Journal Volume
- 27
- Journal Issue
- 6
- Series
- Werkst. Korros.
- Journal Page Range
- 398-403
- ISSN
- 0947-5117
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 7267865
- Subject category
- S37: INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; S36: MATERIALS SCIENCE;
- Is Lead record
- Yes
- Descriptors DEI
- AUSTENITE; CARBIDES; CARBON ADDITIONS; CHROMIUM NITRIDES; CHROMIUM-NICKEL STEELS; CORROSION; HEAT TREATMENTS; MATERIALS TESTING; MICROSTRUCTURE; MOLYBDENUM ALLOYS; NITROGEN ADDITIONS; PHASE STUDIES; PRECIPITATION; SOLUBILITY; STAINLESS STEELS; TRANSITION ELEMENT COMPOUNDS
- Descriptors DEC
- ALLOYS; CARBON COMPOUNDS; CHEMICAL REACTIONS; CHROMIUM ALLOYS; CHROMIUM COMPOUNDS; CHROMIUM STEELS; CORROSION RESISTANT ALLOYS; CRYSTAL STRUCTURE; IRON ALLOYS; IRON BASE ALLOYS; NICKEL ALLOYS; NITRIDES; NITROGEN COMPOUNDS; SEPARATION PROCESSES; STEELS; TESTING; TRANSITION ELEMENT ALLOYS
Optional Information
- Notes
- 11 figs.; 38 refs. Part of a thesis by K.J. Westerfeld.; Updated automatically by Metadata and Full-Text Enrichment Agent