[La(UO2)V2O7][(UO2)(VO4)] the first lanthanum uranyl-vanadate with structure built from two types of sheets based upon the uranophane anion-topology

The new lanthanum uranyl vanadate divanadate, [La(UO2)V2O7][(UO2)(VO4)] was obtained by reaction at 800 °C between lanthanum chloride, uranium oxide (U3O8) and vanadium oxide (V2O5) and the structure was determined from single-crystal X-ray diffraction data. This compound crystallizes in the orthorhombic system with space group P212121 and unit-cell parameters a=6.9470(2) Å, b=7.0934(2) Å, c=25.7464(6) Å, V=1268.73(5) Å3, Z=4. A full matrix least-squares refinement yielded R1=0.0219 for 5493 independent reflections. The crystal structure is characterized by the stacking of uranophane-type sheets 2∞[(UO2)(VO4)]− and double layers 2∞[La(UO2)(V2O7)]+ connected through La–O bonds involving the uranyl oxygen of the uranyl-vanadate sheets. The double layers result from the connection of two 2∞[La(UO2)(VO4)2]− sheets derived from the uranophane anion-topology by replacing half of the uranyl ions by lanthanum atoms and connected through the formation of divanadate entities. - Graphical abstract: A view of the three-dimensional structure of [La(UO2)V2O7][(UO2)(VO4)]. Highlights: ► New lanthanum uranyl vanadate divanadate has been synthesized. ► Structure was determined from single-crystal X-ray diffraction data. ► Structure is characterized by uranophane-type sheets and double layers 2∞[La(UO2)(V2O7)]+.