Preparation of thermal-responsive chitosan-graft-N-isopropylacrylamide membranes via γ-ray irradiation

Poly(N-isopropylacrylamide) (PNIPAAm) has been attracting increasing attention because of its thermosensitivity. Many authors have studied the reaction of chitosan with NIPAAm, with most of the interest being focused on hydrogels. Few research programs, however, were about chitosan membranes grafted with NIPAAm monomer. In this study, a novel thermo-sensitive switching membrane was prepared by radiation-induced simultaneous grafting of NIPAAm onto chitosan membrane. Fourier transform infrared spectroscopy (FT-IR) was used to identify structure of the grafted membranes. Compared to FT-IR spectra of pristine chitosan, the new band at 1535 cm-1 in the grafted membrane was attributed to amide II of PNIPAAm. This indicated that NIPAAm was introduced onto the chitosan membrane. Surface morphology of the grafted membrane was different from the pristine chitosan membrane. The SEM images revealed cypress leaf-like structures adhered tightly to the grafted membrane surface, in comparison to smooth surface of the pristine chitosan membrane. Pure water flux measurements showed that the grafted membrane decreased with the increasing temperature, while water flux of pristine chitosan membrane was constant. It was found that the grafted membrane was sensitive to temperature. The effects of dose, dose rate and the concentration of NIPAAm on the grafting percentage were discussed. The graft yield increased with the monomer concentration and the absorbed dose. (authors)