Production and investigation of thin films of metal actinides (Pu, Am, Cm, Bk, Cf)

Under limited availability of transplutonium metals some special techniques and methods of their production have been developed that combine the process of metal reduction from a chemical compound and preparation of a sample for examination. In this situation the evaporation and condensation of metal onto a substrate becomes the only possible technology. Thin film samples of metallic 244Cm, 248Cm and 249Bk were produced by thermal reduction of oxides with thorium followed by deposition of the metals in the form of thin layers on tantalum substrates. For the production of 249Cf metal in the form of a thin layer the method of thermal reduction of oxide with lanthanum was used. 238Pu and 239Pu samples in the form of films were prepared by direct high temperature evaporation and condensation of the metal onto a substrate. For the production of 241Am films a gram sample of plutonium-241 metal was used containing about 18 % of americium at the time of production. Thermal decomposition of Pt5Am intermetallics in vacuum was used to produce americium metal with about 80% yield. Resistivity of the metallic 249Cf film samples was found to decrease exponentially with increasing temperature. The 249Cf metal demonstrated a tendency to form preferably a DHCP structure with the sample mass increasing. An effect of high specific activity on the crystal structure of 238Pu nuclide thin layers was studied either.