The epoxy resin variation effect on microstructure and physical properties to improve bonded NdFeB flux magnetic density

NdFeB magnets have been fabricated from a mixture of powder NdFeB (MPQ-B+) and epoxy resins (ER) with a variation of 0% wt, 2% wt, 4% wt and 6% wt. The pellets samples were made by pressing 4 tons of the mixture powder at room temperature before curing at 100°C for 1 hour. The SEM-EDX results showed the microstructure with ER were evenly smeared the NdFeB magnetic particles due to higher percent C and lower transition metals value. Sample with 2% wt epoxy resin was able to achieve the highest density of 5.35 g/cm³ and the highest magnetic flux of 2121 Gauss. The magnetic properties characterization using the permagraph indicates that the sample pellets with 2% wt epoxy resin has a value of remanence (Br) = 4.92 kG, coercivity (Hc) = 7.76 kOe, and energy product (Bhmax) = 4.58 MGOe. Despite low remanence value in the pellet samples, the resistance to demagnetization value was still acceptable. (paper)