PNP prototype plant nuclear process heat. Annual report 1983 about the activities in the field of material testing and development
Description
Automatic translation: The research and development work for high-temperature material testing were able to continue as planned in the reporting area in 1983 become. The work extended to corrosion and creep tests in methane reforming gas (process gas), structural stability and processing technology of high-temperature alloys as well as in-company investigations in large-scale test facilities. The corrosion tests included long-term tests with and without intermediate cooling at welded joints up to approx. 5,000 Hours of running time and corrosion tests on creep tests from welded samples of the material NiCr22Col2Mo (INCONEL 617). Significant differences in the corrosion behavior of samples with and without intermediate cooling there were no aging until 5,000 hours ascertain. This means that the oxide layers formed in the withstand general slow temperature changes undamaged, and not by alternately flaking off the oxide layers accelerated corrosion progress.
Abstract (German)
Die Forschungs- und Entwicklungsarbeiten zur Hochtemperatur-Werkstofferprobung konnten im Berichtsraum 1983 planmäßig fortgesetzt werden. Die Arbeiten erstreckten sich auf Korrosions-und Zeitstandversuche im Gas der Methanreformierung (Prozeßgas), Strukturstabilität und Verarbeitungstechnologie von Hochtemperaturlegierungen sowie betriebsbegleitende Untersuchungen in Großversuchsanlagen. Die Korrosionsuntersuchungen umfaßten Langzeitversuche mit und ohne Zwischenabkühlung an Schweißverbindungen bis ca. 5 000 Stunden Laufzeit und Korrosionsuntersuchungen an Zeitstandproben aus geschweißten Proben des Werkstoffs NiCr22Col2Mo (INCONEL 617). Wesentliche Unterschiede im Korrosionsverhalten von Proben mit und ohne Zwischenabkühlung waren bis 5 000 h Auslagerung nicht festzustellen. Dies bedeutet, daß die gebildeten Oxidschichten im allgemeinen langsame Temperaturänderungen unbeschadet überstehen, und es nicht durch abwechselndes Abplatzen der Oxidschichten zu einem beschleunigten Korrosionsfortschritt kommt.
Files
Restricted
The record is publicly accessible, but files are restricted to users with access.
Additional details
Additional titles
- Original title (German)
- PNP Prototypanlage Nukleare Prozeßwärme. Jahresbericht 1983 über die Tätigkeiten auf dem Gebiet der Materialerprobung und -entwicklung
Publishing Information
- Imprint Pagination
- 114 p.
- Report number
- INIS-DE--21M0965
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- International Atomic Energy Agency (IAEA)
- INIS RN
- 53056926
- Subject category
- S21: SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS; S36: MATERIALS SCIENCE;
- Descriptors DEI
- COOLING; CORROSION; CREEP; FEDERAL REPUBLIC OF GERMANY; FORSCHUNGSZENTRUM JUELICH; HTGR TYPE REACTORS; MATERIALS TESTING; METHANE; PROCESS HEAT; PROCESSING; STABILITY; TEMPERATURE RANGE 0400-1000 K; WELDED JOINTS
- Descriptors DEC
- ALKANES; CHEMICAL REACTIONS; DEVELOPED COUNTRIES; ENERGY; EUROPE; GAS COOLED REACTORS; GERMAN FR ORGANIZATIONS; GRAPHITE MODERATED REACTORS; HEAT; HYDROCARBONS; JOINTS; MECHANICAL PROPERTIES; NATIONAL ORGANIZATIONS; ORGANIC COMPOUNDS; REACTORS; TEMPERATURE RANGE; TESTING; WESTERN EUROPE
Optional Information
- Notes
- Document from Juelich Preservation Project; 71 figs., tabs.