Mechanical properties of welded joints of the reduced-activation ferritic steel: 8% Cr-2% W-0.2% V-0.04% Ta-Fe

A reduced-activation ferritic steel, 8Cr-2W-0.2V-0.04Ta-Fe (F-82H) has been developed by JAERI and NKK to improve creep properties and toughness as compared with HT9. The mechanical properties and phase stability of the steel were reported at the previous conferences, ICFRM-2 and 3. This paper is concerned with the mechanical properties of weld metal and welded joints using a newly-developed filler wire of F-82H which contains less C and Ta than the base metal. The design concept of chemical composition of the filter wire was based on a much reduction of activity after irradiation as possible and considerations of the hardenability and toughness of the weld metal. Mechanical properties, such as tensile strength and toughness, of the weld metal and welded joints produced by GTAW after stress-relieving heat treatment were investigated. The results showed that this welding material has almost the same properties as the base metal. (orig.)