Crystallinity and the effect of ionizing radiation in polyethylene. IV. Effect of segregation of low molecular weight chains on determination of main-chain scission in linear polyethylene

Different single crystal preparations of polyethylene with (unfractionated) and without (partially fractionated) low molecular weight chains were irradiated at room temperature. G(crosslink) was determined from the gel point. It is shown that in addition to the molecular weight and molecular weight distribution of polymers, G(crosslink) is determined by three more parameters: thickness of crystalline core, amount of amorphous surface layer, and degree of interlamellar contact. Unlike unfractionated polyethylene, partially fractionated polyethylene showed almost 100 percent gel at about 250 Mrad. To obtain the same amount of gel, unfractionated polyethylene required a much higher dose than that required by partially fractionated polyethylene. Molecular weight distribution of sol fractions of unfractionated and partially fractionated polyethylene was studied by gel permeation chromatography (GPC) and the solubility data analyzed by Charlesby-Pinner plots. It has been shown that the unattainability of 100 percent gel from unfractionated polyethylene is due to segregation of low molecular weight chains during crystallization which need very high doses for complete gelation