Radiochemical synthesis of ^105gAg-labelled silver nanoparticles

A method for synthesis of radiolabelled silver nanoparticles is reported. The method is based on proton activation of silver metal powder, enriched in ¹⁰⁷Ag, with a 30.7 MeV proton beam. At this proton energy ^105gAg is efficiently created, mainly via the ¹⁰⁷Ag(p,3n)¹⁰⁵Cd → ^105gAg reaction. ^105gAg has a half-life of 41.29 days and emits easily detectable gamma radiation on decay to ¹⁰⁵Pd. This makes it very useful as a tracing radionuclide for experiments over several weeks or months. Following activation and a period to allow short-lived radionuclides to decay, the powder was dissolved in concentrated nitric acid in order to form silver nitrate (AgNO₃), which was used to synthesise radiolabelled silver nanoparticles via the process of sodium borohydride reduction. For comparison, non-radioactive silver nanoparticles were synthesised using commercially supplied AgNO₃ in order to check if the use of irradiated Ag powder as a starting material would alter in any way the final nanoparticle characteristics. Both nanoparticle types were characterised using dynamic light scattering, zeta-potential and X-ray diffraction measurements, while additionally the non-radioactive samples were analysed by transmission electron microscopy and UV–Vis spectrometry. A hydrodynamic diameter of about 16 nm was determined for both radiolabelled and non-radioactive nanoparticles, while the electron microscopy on the non-radioactive samples indicated that the physical size of the metal NPs was (7.3 ± 1.4) nm