The mechanical properties of dry, electrospun fibrinogen fibers

Due to their low immunogenicity, biodegradability and native cell-binding domains, fibrinogen fibers may be good candidates for tissue engineering scaffolds, drug delivery vehicles and other medical devices. We used a combined atomic force microscope (AFM)/optical microscope technique to study the mechanical properties of individual, electrospun fibrinogen fibers in dry, ambient conditions. The AFM was used to stretch individual fibers suspended over 13.5 μm wide grooves in a transparent substrate. The optical microscope, located below the sample, was used to monitor the stretching process. Electrospun fibrinogen fibers (diameter, 30–200 nm) can stretch to 74% beyond their original length before rupturing at a stress of 2.1 GPa. They can stretch elastically up to 15% beyond their original length. Using incremental stress–strain curves the viscoelastic behavior of these fibers was determined. The total stretch modulus was 4.2 GPa while the relaxed elastic modulus was 3.7 GPa. When held at constant strain, fibrinogen fibers display stress relaxation with a fast and slow relaxation time of 1.2 s and 11 s. In comparison to native and electrospun collagen fibers, dry electrospun fibrinogen fibers are significantly more extensible and elastic. In comparison to wet electrospun fibrinogen fibers, dry fibers are about 1000 times stiffer. - Highlights: ► Fabricated dry, electrospun, fibrinogen fibers; average diameter, Davg. = 95 nm. ► Determined mechanical properties with combined atomic force/optical microscope. ► Fibers are very extensible (εmax = 74%) and elastic (εelastic = 15%). ► Fiber total modulus, Etot. = 4.2 GPa; elastic modulus, Eel. = 3.7 GPa. ► Fiber stress relaxation times: τ1 = 1.2 s and τ2 = 11 s.