Comparison of wear behaviour and mechanical properties of as-cast Al6082 and Al6082-T6 using statistical analysis

In the present work the wear behavior and mechanical properties of as cast A16082 and A16086-T6 were compared and analyzed using statistical analysis. The as cast Al6082 alloy was solutionized at 550°C, quenched and artificially aged at 170°C for 8hrs. Metallographic examination and XRD analysis revealed the presence of intermetallic compounds Al₆Mn.Hardness of heat treated Al6082 was found to be more than as cast sample. Wear tests were carried out using Pin on Disc wear testing machine according to Taguchi L9 orthogonal array. Experiments were conducted under normal load 10-30N, sliding speed 1-3m/s, sliding distance 400,800,1200m respectively. Sliding speed was found to be the dominant factor for wear in both as cast and aged Al 6082 alloy. Sliding distance increases the wear rate up to 800m and then after it decreases. (paper)