Synthesis of encapsulated pigments based on Fe, Co and Si by route of polymeric precursors

The objective is to apply the polymeric precursor method to obtain encapsulated pigments, the basis of oxides of iron and cobalt deposited on silica. The method has advantages such as reduction of time and reproducibility in the conventional methods, and also improves optical properties, thermal stability and morphology. The synthesis was based on the dissolution of the citric acid (complexing agent), addition of oxides of iron and cobalt (ions chromophores) polymerization of ethylene glycol and silica coating. The mixture was pre-calcined to form the precursor powder was analyzed by TG and DTA. Was then split, and calcined at different temperatures (700 ° C - 900 ° C) and analyzed by BET, DRX, MEV and UV-Visible. The pigments were stable thermally, with surface area ranging between 3,09 and 7,65 m² / g, formation of crystalline phases of cobalt ferrite (CoFe₂O₄) and Cristobalite (SiO₂) and agglomerates of particles slightly rounded. (author)