Influence of the angle between cold rolling direction and hot rolling direction on the texture evolution of non-oriented electrical steels

In processing non-oriented electrical steel sheets using conventional rolling schemes, the most common texture components obtained after final annealing are the magnetically unfavourable <111>//ND (γ) and <110>//RD (α) fibres. A lot of researches have been carried out trying to optimize the processes to produce the favourable <001>//ND (θ) fibre. However, since the final texture is formed through a series of texture evolution steps during the solidification, hot rolling, cold rolling and annealing processes, it is quite challenging to tailor the texture of the final product. In this study, a new rolling scheme was examined, in which the cold rolling direction (CRD) was inclined to the hot rolling direction (HRD) at an angle from 0° to 90° (with a 15° increment). This was intended to alter the texture commonly produced by cold rolling along the HRD, and to optimize the final recrystallization texture. The cold rolling and recrystallization textures of two non-oriented electrical steels with 0.9% and 2.8% Si were measured. It was found that the inclination of CRD to HRD has a substantial effect on the cold rolling texture for both steels, but only in the low Si steel, does it lead to significantly different recrystallization textures. A strong cube texture was produced at an inclination angle of 60°, and the <111>//ND (γ) fibre was significantly weakened or essentially disappeared. The core losses of these steels were measured by Epstein frame method and the results showed a ∼10% difference among strips cold rolled at different angles. A minimum core loss occurred at a 45° inclination angle in the low Si steel. (paper)