Microstructural evaluation of Ni-graphite composites sintered from NiO-SiC powder mixtures

Nickel alloys and composites are interesting engineering materials as a result of a combination of mechanical, corrosion and wear resistance at service temperatures that exceed those of steels and steel-based materials. The present study aimed at sintering Ni-graphite composites from NiO-SiC mixtures and investigate the in-situ formation of graphite. NiO powders were mixed with SiC (0, 3, 5 and 10 wt.%) and attrition-milled during 1 h. The mixtures were then granulated using 1.5 wt.% paraffin in hexane solution and uniaxially pressed under 400 MPa. The cylindrical pellets were then sintered at 1200 ° C. The sintered materials were characterized by density measurements, dilatometric and microstructural analyses, as well as Vickers microhardness. The results showed that Ni-graphite composites were successfully produced from NiO-SiC mixtures with full reduction of NiO and dissociation of SiC to form a Ni-Si matrix and graphite nodules. (author)