Texture of tungsten monocrystals after rolling in profiled rolls

Using the method of reverse polar figures (RPE) in MoKsub(α)-radiation the texture of monocrystals with initial orientations [100] < 100 > and [110] < 100 >, rolled at strains 0-9g and 0-50% respectively, has been studied. It is shown that reorientation of rolling direction is realized by means of crystallite rotation around the normal to the walls of roll pass from < 100 > → < 114 > → < 130 > → < ( 110 >. The final orientation of rolling direction < 110 > is not achieved even at the deformation with a 90% reduction