Study of deformation and fracture micro mechanisms of titanium alloy Ti-6Al-4V using electron microscopy and and X-ray diffraction techniques

This present work allowed the study of deformation and fracture micro mechanisms of titanium alloy Ti-6Al-4V, used commercially for the manufacture of metallic biomaterials. The techniques employed for the analysis of the material under study were: scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray diffraction (XRD). The study of the influence and behavior of the phases present in titanium alloys is important to evaluate the behavior of cracks in titanium alloys with high mechanical strength, which have fine alpha (α), beta (β) and (α±β) microstructure, linking the presence of the phases with the strength of the material. The evaluation in situ of deformation and fracture micro mechanisms were performed by TEM and was also a study of phase transformations during cooling in titanium alloys, using the techniques of bright field, dark field and diffraction of electrons in the selected area. After heat treatment differences were observed between the amount of in relation to the original microstructure of the β and α phases material for different conditions used in heat treatment applied to the alloy. The presence of lamellar microstructure formed during cooling in the β field was observed, promoting the conversion of part of the secondary alpha structure in β phase, which was trapped between the lamellar of alpha. (author)