Structural, magnetic and luminescent characteristics of Pr3+-doped ZrO2 powders synthesized by a sol-gel method

The structural, magnetic and luminescence properties of praseodymium-doped zirconia powders of compositions Pr0.03Zr0.97O2 and Pr0.05Zr0.95O2 synthesized by a sol-gel process have been investigated. X-ray diffraction patterns indicate that these materials crystallize in a tetragonal fluorite-type structure. Scanning electron microscopy shows that the powders exhibit an agglomerated microcrystalline structure and the grain size may be in the order of 5-20 μm. The study of the magnetic properties of these doped metal oxides indicates a Curie-Weiss behaviour in the temperature range (100-300) K that allow us to estimate an effective magnetic moment of 3.51 μB, which indicates the presence of Pr3+ in the grown samples. Cathodoluminescence spectra recorded at temperatures between 85 and 295 K show emission peaks that can be attributed to transitions between different states within the 4f2 configuration of Pr3+ ions incorporated in the zirconia crystal lattice. Thermoluminescence measured at temperatures ranging from 373 to 773 K and at 550 nm wavelength show an intense and broad peak around 653 K for the Pr-doped zirconia which is not observed in the undoped material.