Agglomeration in core-shell structure of CuAg nanoparticles synthesized by the laser ablation of Cu target in aqueous solutions

Metallic copper Cu and bimetallic copper–silver CuAg nanoparticles (NPs) are generated by the ablation of copper bulk target in water and aqueous Ag colloidal solution, respectively. The experiments were performed using nanosecond Nd:YAG laser operating at 1064 nm. The generated NPs are characterized by UV–vis absorption spectroscopy, laser-induced breakdown spectroscopy, dynamic light scattering and scanning electron microscopy. The conducted investigations can be summarized as follows: (i) CuAg NPs colloidal solution possess the absorption in UV–vis spectral region, which can be attributed to the Cu-component; (ii) the primary bimetallic CuAg NPs have near uniform dimensions with diameter of about 15 nm, and as a rule, they are grouped into larger agglomerates without defined morphology; (iii) the obtained Cu NPs have mainly spherical form with average diameters up to 20 nm. Both types of NPs show a tendency towards the formation of large agglomerates with different morphology. Bimetallic NPs show the plasmon resonance in the vicinity of 640 nm with a good coincidence with formation of the colloidal solution of pure Cu NPs. The results also demonstrate that the core–shell structure (Ag-rich core/Cu-rich shell) is important for the formation of the bimetallic NPs, also agreeing very well with theory. (paper)