γ radiation thermoluminescence performance of HFCVD diamond films

Polycrystalline chemically vapor deposited (CVD) diamond films have been proposed as detectors and dosimeters of ionizing radiation with prospective applications in high-energy photon dosimetry applications. We present a comparison study on the thermoluminescence (TL) properties of two diamond film samples grown by the hot filament CVD method having thickness of 180 and 500 μm and exposed to γ radiation in the 1-300 Gy dose range. The 180 μm thick sample deposited on silicon substrate displayed a TL glow curve peaked at 145 deg. C. The 500 μm, which was a free standing sample, exhibited higher intensity and a well defined first order kinetics TL glow peak around 289 deg. C. Both diamond samples showed a linear dose behavior in the 1-50 Gy range and sublinear behavior for higher doses. The 180 and 500 μm samples presented about 80% and 30% TL losses in a 24 h period, respectively, with both samples showing excellent TL reproducibility. The results indicate that the 500 μm CVD diamond film exhibited a good TL behavior adequate for γ radiation dosimetry