Qualification of reconstituted Charpy-specimens after DIN- and ASTM-standards
Creators
- 1. Siemens AG/KWU, Erlangen (Germany)
- 2. Ingenieurschule fuer Maschinenbau, Bautzen (Germany)
Description
The comparison between DIN- and ASTM-tests has shown that the higher ASTM-Charpy values in the high-value range are due to large deformations in the impact area of the peen. These deformations do not occur in reconstituted specimens, as the are prevented by the hard HAZ. Thus, the DIN- and ASTM-results are equal. In consequences of the higher initial values in ASTM-compact specimens, however, there is a greater drop in Charpy work. Taking this into account the ASTM-values as well are to be accepted. (orig.)
Abstract (German)
Fuer den Vergleich zwischen DIN- und ASTM-Pruefung gilt, dass die hoeheren ASTM-Kerbschlagwerke im Hochlagenbereich auf staken Verformungen im Auftreffbereich der Finne zurueckzufuehren sind. Bei den Verbundproben treten diese Verformungen nicht auf, weil sie durch die harte WEZ verhindert werden. Die DIN- und ASTM-Ergebnisse sind somit gleich. Wegen der hoeheren Ausgangswerte bei ASTM-Kompaktproben ist aber der Abfall der Kerbschlagarbeit groesser. In Kenntnis dieses Sachverhaltes sind auch ASTM-Werte zu akzeptieren. (orig.)Additional details
Additional titles
- Original title (German)
- Qualifizierung von Kerbschlagbiege-Verbundproben im Vergleich zwischen DIN-und ASTM-Normen
Publishing Information
- Imprint Title
- Safety and reliability of plant technology with special emphasis on nuclear technology. Papers. Vol. 1
- Imprint Pagination
- 600 p.
- Journal Page Range
- p. 7.1-7.19.
Conference
- Title
- Safety and reliability of plant technology with special emphasis on nuclear technology - ageing mechanisms and potential for energy absorption in piping systems.
- Original Conference Title
- 17. MPA-Seminar: Sicherheit und Verfuegbarkeit in der Anlagentechnik mit dem Schwerpunkt Kerntechnik - Rissausloesende Faktoren und Potential fuer Energieaufnahme in Rohrleitungssystemen
- Acronym
- 17. MPA-seminar
- Dates
- 10-11 Oct 1991.
- Place
- Stuttgart (Germany).
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 26009730
- Subject category
- S36: MATERIALS SCIENCE;
- Resource subtype / Literary indicator
- Conference, Non-conventional Literature
- Descriptors DEI
- BRITTLENESS; CHARPY TEST; COMPARATIVE EVALUATIONS; ELECTRON BEAM WELDING; MECHANICAL PROPERTIES; STANDARDIZATION; WELDED JOINTS
- Descriptors DEC
- DESTRUCTIVE TESTING; EVALUATION; FABRICATION; IMPACT TESTS; JOINING; JOINTS; MATERIALS TESTING; MECHANICAL TESTS; TESTING; WELDING
Optional Information
- Notes
- Imprint:Sicherheit und Verfuegbarkeit in der Anlagentechnik mit dem Schwerpunkt Kerntechnik. Vortraege. Bd. 1.