Determination of the mechanical characteristics of irradiated metals from the results of microhardness tests

To predict the possibilities of using structural materials in nuclear and thermonuclear reactors, it is important to have data on changes of the mechanical characteristics and irradiation obtained from full-scale or simulation tests. Materials are irradiated in nuclear reactors with fast neutrons, the sources of high-energy neutrons with an energy of 14 MeV and the accelerators of charged particles. The restricted volumes for irradiation of these specimens in the systems and also the need to test large numbers of specimens under the same conditions make it necessary to reduce the size of irradiated specimens. To solve this problem, work is being carried out to develop various methods of testing miniature specimens, including tension extrusion of disc-shaped micro-specimens, microhardness, and the Charpy Method. In examination of the irradiation hardening of the materials, the main advantage of the microhardness method is that it makes it possible to examine small specimens. In single microhardness tests, only a small area of the irradiated specimens is examined. This makes it possible to increase the radiation dose and carry out subsequent tests of microhardness on the same specimens. The aim of this work was to determine the possibilities of using the microhardness measurement method for evaluating the mechanical characteristics of metallic materials. The comparison of the data, obtained in microhardness tests and in tensile loading specimens of 0Kh18N10Tsteel, irradiated with neutrons, shows the efficiency of the microhardness method as a tool for investigating the irradiation hardening of reactor materials