Structural phase transitions of high-pressure LixNa1-xNbO3 solid solutions
Creators
- 1. Inst. Fiziki Tverdogo Tela i Poluprovodnikov Natsional'noj Akademii Nauk Belorussii, Minsk (Belarus)
- 2. Inst. Khimii i Tekhnologii Redkikh Ehlementov i Mineral'nogo Syr'ya KNTs Rossijskoj Akademii Nauk, Apatity (Russian Federation)
Description
Solid solutions of LixNa1-xNbO3 with x=0.125, 0.17, 0.25 are synthesized at high pressures (6 GPa) and temperatures (1100-1500 Deg C) and their X-ray diffraction studies are performed. The sequence of polymorphic transformations depending on composition and temperature is determined for the solid solutions obtained. For discovered polymorphic modifications the concentration and temperature dependences of crystal lattice parameters are presented. It is shown that under standard conditions the solid solutions synthesized at high pressure with x=0.17 and 0.25 are supersaturated ones, and on heating above ≅800 Deg C a LiNbO3 base phase precipitates in given systems
Abstract (Russian)
При высоких давлениях (6 ГПа) и температурах (1100-1500 град С) синтезированы твердые растворы LixNa1-xNbO3 с x=0.125, 0.17, 0.25 и проведены их рентгеноструктурные исследования. Для получения твердых растворов установлена последовательность полиморфных переходов в зависимости от состава и температуры. Приводятся концентрационные и температурные зависимости параметров кристаллической решетки для выявленных полиморфных модификаций. Показано, что при нормальных условиях твердые растворы, полученные при высоком давлении, с х=0.17 и 0.25 являются пересыщенными, и при нагревании выше ≅800 град С в данных системах выделяется фаза на основе LiNbO3Additional details
Additional titles
- Original title (Russian)
- Структурные фазовые переходы в твердых растворах Ли
Publishing Information
- Journal Title
- Neorganicheskie Materialy
- Journal Volume
- 40
- Journal Issue
- 9
- Journal Page Range
- p. 1110-1114
- ISSN
- 0002-337X
- CODEN
- NEOMB8
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 37020163
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- CONCENTRATION RATIO; CRYSTAL-PHASE TRANSFORMATIONS; LATTICE PARAMETERS; LITHIUM COMPOUNDS; NIOBATES; PHASE STUDIES; PRESSURE RANGE GIGA PA; SODIUM COMPOUNDS; SOLID SOLUTIONS; SYNTHESIS; TEMPERATURE RANGE 0400-1000 K; TEMPERATURE RANGE 1000-4000 K
- Descriptors DEC
- ALKALI METAL COMPOUNDS; DIMENSIONLESS NUMBERS; DISPERSIONS; HOMOGENEOUS MIXTURES; MIXTURES; NIOBIUM COMPOUNDS; OXYGEN COMPOUNDS; PHASE TRANSFORMATIONS; PRESSURE RANGE; REFRACTORY METAL COMPOUNDS; SOLUTIONS; TEMPERATURE RANGE; TRANSITION ELEMENT COMPOUNDS
Optional Information
- Notes
- 8 refs., 4 figs.