Analyses on the U-Mo/Al Chemical Interaction and the Effects of Diffusion Barrier Coatings

While many HEU-fueled research reactors have been converted by adopting LEU U3Si2 fuel in harmony with the Reduced Enrichment for Research and Test Reactors (RERTR) program, some high performance research reactors still need the development of advanced fuels with higher uranium densities. Currently, gamma-phase U-Mo alloys are considered promising candidates to be used as high uranium density fuel for the high performance reactors. For the production of UMo alloy powder, the centrifugal atomization technology developed by KAERI has been considered the most promising way because of high yield production and excellent powder quality when compared with other possible methods such as grinding, machining or hydriding-dehydriding. However, severe pore formation associated with an extensive interaction between the U-Mo and Al matrix, although the irradiation performance of U-Mo itself showed most stable, delay the fuel qualification of UMo fuel for high performance research reactors. Because the reaction products, i.e. uranium aluminides (UAlx), is less dense than the mixed reactants, the volume of the fuel meat increases after formation of interaction layer(IL). In addition to the impact on the swelling performance, the reaction layers between the U-Mo and Al matrix induces a degradation of the thermal conductivities of the U-Mo/Al dispersion fuels. The chemical interaction between the U-Mo and Al matrix are analyzed in this study to find remedies to reduce the growth of the interaction layers during irradiation. In addition, various coating technologies for the formation of diffusion barriers on U-Mo particles are proposed as a result of the analyses