Crack growth behaviour of a low alloy boiler steel in high temperature water containing oxygen, under static load

Creators

  • 1. Stuttgart Univ. (Germany, F.R.). Staatliche Materialpruefungsanstalt

Description

The crack growth behaviour of the strong material 17 Mn MoV 6 4 in pure high temperature water containing oxygen was examined for the case of static load. The water conditions produced in the autoclave were 8 ppm oxygen content at a pressure of 70 bar and a temperature of 240deg C in quasi-stagnant flow conditions. Due to fractographic examination of the fracture surfaces, the crack formation found can be assigned to 'strain-induced crack corrosion'. (orig./DG)

Availability note (English)

Available from Stuttgart Univ. (Germany, F.R.). Staatliche Materialpruefungsanstalt.

Abstract (German)

Das Risswachstumsverhalten des hoeherfesten Werkstoffs 17 MnMoV 6 4 in sauerstoffhaltigem reinem Hochtemperaturwasser wurde fuer den Fall statischer Belastung untersucht. Die im Autoklaven realisierten Wasserbedingungen waren 8 ppm Sauerstoffgehalt bei 70 bar Druck und einer Temperatur von 240deg C mit quasistagnierenden Stroemungsbedingungen. Aufgrund fraktografischer Bruchflaechenuntersuchung koennen die gefundenen Rissbildungen der 'Dehnungsinduzierten Risskorrosion' (DRK) zugeordnet werden. (orig./DG)

Additional details

Additional titles

Original title (German)
Risswachstumsverhalten eines niedriglegierten Kesselbaustahles in sauerstoffhaltigem Hochtemperaturwasser unter statischer Belastung

Publishing Information

Imprint Title
Safety and reliability of plant technology with special emphasis on long-term integrity of pressure components of nuclear power plants. Vol. 1 and 2
Imprint Pagination
1003 p.
Journal Page Range
p. 21.1-21.29.

Conference

Title
Long-term integrity of pressure components of nuclear power plants.
Original Conference Title
14. MPA-Seminar ueber Sicherheit und Verfuegbarkeit in der Anlagentechnik: Langzeitintegritaet der Druckfuehrenden Bauteile von Kernkraftwerken
Acronym
14. MPA-seminar on safety and reliability of plant technology
Dates
6-7 Oct 1988.
Place
Stuttgart (Germany, F.R.).

INIS

Country of Publication
Germany
Country of Input or Organization
Germany
INIS RN
21013486
Subject category
S36: MATERIALS SCIENCE; S36: MATERIALS SCIENCE; S22: GENERAL STUDIES OF NUCLEAR REACTORS;
Resource subtype / Literary indicator
Conference, Non-conventional Literature
Descriptors DEI
CRACK PROPAGATION; HIGH PRESSURE; HIGH TEMPERATURE; LOW ALLOY STEELS; PRESSURE VESSELS; REACTOR COMPONENTS; STRESS CORROSION
Descriptors DEC
ALLOYS; CARBON ADDITIONS; CHEMICAL REACTIONS; CONTAINERS; CORROSION; IRON ALLOYS; IRON BASE ALLOYS; STEELS

Optional Information

Notes
Imprint:Published in 2 separate volumes.;Sicherheit und Verfuegbarkeit in der Anlagentechnik mit dem Schwerpunkt 'Langzeitintegritaet der druckfuehrenden Bauteile von Kernkraftwerken'. Bd. 1 und 2.;Bd. 1: Anlagentechnik, Thermoschock, strahleninduzierte Versproedung, Korrosion/Verschleiss, zerstoerungsfreie Pruefung. Bd. 2: Zeitstandverhalten/Kriechvorgaenge, Behaelter- und Komponenten-Integritaet, Rohrleitungsverhalten.