Manufacture of sintered silicon nitrides

Sintered silicon nitrides are manufactured by sintering Si3N powder containing 2 to 15% in wt of a powder mixture composed of nitride powder of lanthanide or Y 100 parts and AIN powder less than 100 parts at 1500 to 1900 deg. temperature under a pressure of less than 200 Kg/sq. cm. The sintered Si3N has high mechanical strength in high temperature. Thus, Si3N4 93.0, Y 5.0 and AlN 2.0% in weight were wet mixed in acetone in N atom, molded and sintered at 1750 deg. and 1000 Kg/sq. cm. to give a sintered body having high hardness