Infrared spectroscopy and thermal analysis of prepared cation exchangers from cellulosic materials

Different cation exchangers were prepared by incorporation of phosphate and sulfate groups into acid or alkali treated wood pulp. The molecular structure of these cation exchangers were followed by infrared spectroscopy and thermal degradation analysis technique. From infrared spectra, a new bands are seen at 1200 and 980 cm-1 in phosphorylated wood pulp due to the formation of C-O-P bond. Another bands were seen at 1400, 1200 and 980 cm-1 in phospho sulfonated wood pulp due to the formation of CO- P and C-O-S bonds. Also, it is seen from infrared spectra that the crystallinity index for acid treated wood pulp has a higher value than untreated and alkali treated wood pulp. On the other hand, the acid treated and phosphorylated acid treated wood pulp have a higher activation energy than untreated and phosphorylated alkali treated wood pulp