Study of peculiarities of hydrogen isotopes mixture permeation through low activated steel F82H

Full text: The problem of diffusion tritium leakage through blanket materials of future fusion device makes some constructive difficulties concerned with protection of personnel and environment and also with losses of tritium, which is planned to be used in the same device. One of the little-studied problems in the tritium leakage process in Fusion Power Plant is that in fact tritium will penetrate through materials while other hydrogen isotopes are present. These are deuterium and hydrogen which always are present in metals. Therefore, for evaluation of tritium leakage in future Fusion Power Plant under such conditions it is necessary to have experimental data about permeation of these hydrogen isotopes through the structure materials.One of proposed structure materials of fusion reactor blanket is low activated steel F82H. The experiment results on evaluation of .hydrogen, deuterium and its mixture interaction parameters with steel F82H are shown in this work. The tests were carried out within temperature range 273-973 K under inlet hydrogen pressure of 100-2000 Pa. Diffusivity, deuterium and hydrogen permeation constants for low activated steel F82H was determined from experiment results. Those experimental results were used for created phenomenology model which describes hydrogen isotope penetration through tube sample from hydrogen isotopes mixture. That model was used so determining the ratios of desorption rates (D-D, D-H, H-H) on outlet side of sample. Using of so obtained results, we can correctly evaluate, the titanium leakage from blanket of fusion machine which will be constructed using low activated steel F82H