Superconducting YBa2Cu3O6.8 films on metallic substrates using in situ laser deposition
- 1. New York State Institute on Superconductivity, State University of New York at Buffalo, Bonner Hall, New York 14260 (USA)
Description
In situ laser deposition was used to fabricate YBa2Cu3O6.8 (YBCO) films on metallic substrates. With a buffer layer, YBCO films were strongly c-axis oriented. Tc = 83 K and Jc= 4000 A/cm2 at 77 K were obtained for a 0.5 μm YBCO film with a 0.15 μm yttrium-stabilized ZrO2 buffer layer. There was negligible interdiffusion occurring at the interfaces. The n value of YBCO films ranged from 1.4 to 1.5
Additional details
Publishing Information
- Journal Title
- Applied Physics Letters
- Journal Volume
- 56
- Journal Issue
- 26
- Series
- Appl. Phys. Lett.
- Journal Page Range
- 2684-2686
- ISSN
- 0003-6951
- CODEN
- APPLA
INIS
- Country of Publication
- United States
- Country of Input or Organization
- United States
- INIS RN
- 21086207
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- BARIUM OXIDES; COPPER OXIDES; CRITICAL CURRENT; CRYSTALLIZATION; DEPOSITION; LASER RADIATION; SUPERCONDUCTING FILMS; SUPERCONDUCTIVITY; TRANSITION TEMPERATURE; YTTRIUM OXIDES
- Descriptors DEC
- ALKALINE EARTH METAL COMPOUNDS; BARIUM COMPOUNDS; CHALCOGENIDES; COPPER COMPOUNDS; CURRENTS; ELECTRIC CONDUCTIVITY; ELECTRIC CURRENTS; ELECTRICAL PROPERTIES; ELECTROMAGNETIC RADIATION; FILMS; OXIDES; OXYGEN COMPOUNDS; PHASE TRANSFORMATIONS; PHYSICAL PROPERTIES; RADIATIONS; THERMODYNAMIC PROPERTIES; TRANSITION ELEMENT COMPOUNDS; YTTRIUM COMPOUNDS