Synergistic effect and mechanism of platinum catalyst and nitrogen-containing silane on the thermal stability of silicone rubber

Highlights: • Platinum (Pt) and nitrogen-containing silane (NS) were introduced into silicone rubber. • The thermal stability was improved by Pt/NS both under nitrogen and air atmosphere. • The TG-FTIR of evolved gases during degradation was performed. • The synergistic effect and mechanism of Pt and NS were proposed. - Abstract: Platinum (Pt) catalyst and nitrogen-containing silane (NS) were introduced to improve the thermal stability of silicone rubber. The effects of Pt and NS on thermal stability and degradation mechanism of silicone rubber were investigated by thermogravimetry (TG), thermogravimetry-Fourier transform infrared spectrometry (TG-FTIR), scanning electron microscope-energy dispersive X-ray spectroscopy (SEM-EDXS) and Fourier transform infrared spectrometry (FTIR). A significant synergism was found between Pt and NS for improving the thermal stability of silicone rubber. When 6.67 ppm of Pt and 1.4 phr of NS were introduced, the temperature of 10% and 20% weight loss under nitrogen atmosphere were respectively increased by 36 °C and 119 °C. Meanwhile, the residue weight at 900 °C was doubled to 68% in the presence of Pt/NS. The synergistic mechanism might be that the nitrogen atom coordinated with Pt and improved the catalytic efficiency of Pt. Additionally, NS preserved the catalytic activity of Pt under air atmosphere. Hence, Pt/NS efficiently catalyzed thermal crosslinking and suppressed degradation of silicone chains. Moreover, it revealed that the presence of Pt/NS protected silicone chains from oxidation. Thus, the unzipping depolymerization by silanol groups was reduced significantly.