Electrochemical behaviour of ceramic yttria stabilized zirconia on carbon steel synthesized via sol-gel process

Chromate conversion coatings have been widely applied for the corrosion of different metallic substrates. However, the waste containing Cr6+ has many limitations due to the environmental consideration and health hazards. An interesting alternative seems to be the deposition on metallic surface of thin layers of yttria or zirconia or both by the sol-gel process. In this study, Ytttria and Yttria stabilized zirconia (YSZ, 8% Y2O3) thin films were used for coating commercial carbon steel substrates by sol-gel method and the dip-coating process. The evolution of organic compounds up to crystallization process as a function of heat treatments was study by FT-IR spectroscopy. The structure and morphology of the coatings were analysed using X-ray diffraction (XRD) and scanning electron microscopy (SEM). The anticorrosion performance of the coatings has been evaluated by using electrochemical techniques in an aggressive media (3.5 wt.% NaCl). The corrosion behaviour of sol-gel method was compared with traditional chromate conversion coatings. Differences in the electrochemical behaviour of YSZ coatings are related to the development of microcracks during the sintering process and to the presence of organic compounds during growth film. Electrochemical results showed that sol-gel YSZ and Y2O3 coatings can act as protective barriers against wet corrosion; however yttria films displayed low adhesion to substrate. The corrosion parameters provide an explanation of the role of each film and show a considerable increase in the corrosion resistance for coated samples in comparison to the bare steel samples.