The effect of tempering on mechanical properties of 50Mn18Cr4WN retaining ring material

50Mn18Cr4WN is a retaining ring steel. It is strengthened by solution heat treatment and cold working. The process produces high macro residual stress. The retaining ring must be tempered for stress-relief. When the ring is sleeved, it is heated too. If the retaining ring is tempered, are the mechanical properties of the retaining ring damaged? The problem is described in the article. The tempering of testing pieces was carried out at several temperatures: 350degC, 400degC, 450degC, 500degC and 650degC. The tempering time was 3h. The yield point, tensile strength, elongation and reduction of area were determined by means of the tensile test. In the results, for temperatures between 350degC and 450degC, the yield point, tensile strength, elongation and reduction of area did not change notably. A stress corrosion cracking test was also carried out in a 3%Ni4NO3, 36%Ca(NO3)2 aqueous solution. K1scc values after tempering at 450degC and without tempering were measured. The results showed that the K1scc after tempering at 450degC decreased notably. Micrographs show that carbo-nitride precipitated. The precipitated carbo-nitride particles increased in size at the grain boundaries. The precipitated carbonitride particles increased in number at slip lines. It is clear that the precipitated particles lead to the increase of micro-cells and the micro-cells aggravated the stress corrosion cracking process. (orig.)