Chain conformations of the component polymers and the microphase separation structures of homopolymer/block coplymer blends

Microdomain spacings of lamellar structures formed by styrene homopolymer/styrene-2-vinylpyridine diblock copolymer/2-vinylpyridine homopolymer blends were measured by small-angle X-ray scattering (SAXS) and single chain conformations of block copolymers in the same blend system were measured by small-angle neutron scattering (SANS). The molecular weight of diblock copolymers is 78K-72K, and three kinds of styrene homopolymer (SH) and 2-vinylpyridine homopolymer (PH) pairs were blended, their molecular weight ratios to that of host block chains were 0.17, 0.38, and 0.78, respectively. Two blend ratios of homopolymer (H)/block copolymer (B), i.e. 1/2 and 1/1 were examined. It was found that the domain spacings of all blends are larger than that of pure block copolymer and that they are increasing with increasing the molecular weight of homopolymers and/or with increasing the volume fraction of homopolymers. Further, block chains in the blends were confirmed to have almost the same chain dimension as that of block chain in pure block copolymer system in the direction parallel to the domain interface irrespective of molecular weight and volume fraction of homopolymers. (author)