Comparative study of the thermoluminescence between the materials α-Al2O3:C, KCl:Eu2+, KBr: Eu2+ and VYCOR

It is presented some investigation results related to the thermoluminescence curves (Tl), Tl emission and the spectra of excitation of thermoluminescence in the ultraviolet region of 190 to 250 nm in the materials α-Al2O3:C, KCl: Eu2+, KBr: Eu2+ and the Vycor glass. It was able to be observed that the Tl emission for the first three materials exists around 420 nm and in the case of Vycor the emission consists of two Tl peaks where the most low temperature is a band more wide centered in 460 nm and the other band of high temperature emits in 470 nm. In the excitation curves of Tl were obtained centered bands around 230 nm for KCl: Eu2+, 235 nm for KBr: Eu2+, 220 nm for the alumina and 195 nm for the Vycor. From the results it was able to be appreciated that this last has a minor relative intensity with respect to the others materials but also the region in which works there was an alone band between the 190 to 205 nm. This fact makes the material be very selective in the ultraviolet region of greatest energy. (Author)