The Study of the Influence of Urea and Hexa Methylene Tetramine (HMTA) Additive on the Total Gelation Process of Uranium on the Chemical Characteristic of the Poly (Uranate-Vinyl Alcohol) Gel

The study of the influence of urea and Hexa methylene tetramine (HMTA) additive on the total gelation process of uranium on the chemical characteristic of the poly (uranate-vinyl alcohol) gel was done. First of all the 1M uranyl nitrate solution was heated at 70 °C, then variation the 1,2,3,4 and 5M urea additive was studied. Urea was added to the hot solution, and stirred for 10 minutes, producing the colloid particles of UO3. The mixing and heating up for 20 minutes, the colloid of UO3 solution reacted by mixed of THF-PVA 1:1 solution. The solution was cooled at 32°C for 2 hours, and then variation the 1,2,3,4 and 5M HMTA additive was studied. HMTA was added into solution at 32°C and was stirred to form the homogenous sol solution. For the poly (urinate-vinyl) gel formation, the sol solution was dropped to the medium solution of 5M NH5OH at ambient condition. Gel formatted was microsphere then soaked, washed by NH4OH and hot water to release the chemical matters which were unreacted, was dried at 60°C and then dried at 150°C for 4 hours. The chemical characteristic of gel was made, covering the analyzed of colour, shape and diameter microsphere using optical microscope. Next, the analysis of molecular composition of the gel, using Fourier transform infra red spectroscopic (FTIR), was made. The analytical were the qualitative analysis of the absorption band of infra red spectrum on O-U-O-U-O bond, U-O bond and NH3, C-OH, C-H and OH functional group at 300-4000 wave numbers. The result of the research showed that the addition of urea and HMTA additive influences on chemical characteristic of the poly (uranate-vinyl alcohol) gel. The optimum condition was at 2-3 M urea and 2- M HMTA concentration. The analyze of absorption band of infra red spectrum showed that the molecular composition of poly (vinyl alcohol) gel was the uranium trioxide, ammonia, water and polyvinyl alcohol molecular contain with the molecular formulas of [2UO3.2 NH3.H2O.PVA]. (author)